"The contamination caused what is known as a hard alpha inclusion, where a contaminant particle in a metal alloy causes the metal around it to become brittle. The brittle titanium around the impurity then cracked during forging and fell out during final machining, leaving a cavity with microscopic cracks at the edges. For the next 18 years, the crack grew slightly each time the engine was powered up and brought to operating temperature. Eventually, the crack broke open, causing the disk to fail."